Q420
作者：上海科涅金属 时间：2023-12-01 浏览：155对应牌号：Q420、Grade60[415]、SEV295、S420NL、1.8912、S420ML、1.8836、HS420D
Q420A化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.035 | ≤0.035 | ≤0.8 | ≤0.2 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 |
Q420B化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.035 | ≤0.035 | ≤0.8 | ≤0.2 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 |
Q420C化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.03 | ≤0.03 | ≤0.8 | ≤0.2 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
Q420D化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.025 | ≤0.03 | ≤0.8 | ≤0.2 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
Q420E化学成分：
C | Si | Mn | Cr | S | P | Ni | Mo | Cu | Nb | V | Ti | N | ALs |
≤0.2 | ≤0.5 | ≤1.7 | ≤0.3 | ≤0.02 | ≤0.025 | ≤0.8 | ≤0.2 | ≤0.3 | ≤0.07 | ≤0.2 | ≤0.2 | ≤0.015 | ≥0.015 |
力学性能：
【抗拉强度】（σb/MPa）
520～680
【伸长率】（δ5/%）
等级 | δ5/% |
A | ≧18 |
B | ≧18 |
C | ≧19 |
D | ≧19 |
E | ≧19 |
【屈服点】（σs/MPa）
厚度（直径、边长）/mm | ≦16 | >16～35 | >35～50 | >50～100 |
σs/MPa | ≧420 | ≧400 | ≧380 | ≧360 |
【冲击吸收功】（Akv（纵向）/J）
等级￤温度 | +20℃ | 0℃ | -20℃ | -40℃ |
A |
|
|
|
|
B | ≧34 |
|
|
|
C |
| ≧34 |
|
|
D |
|
| ≧34 |
|
E |
|
|
| ≧27 |
特性及应用：
Q420具有高的强度，良好的抗疲劳性能；高韧性和低的脆性转变温度；良好的冷成型性能和焊接性能；具有较好的抗腐蚀性能和一定的耐磨性能。强度高，特别是在正火或正火加回火状态有较高的综合力学性能。
大型船舶、桥梁、电站设备、中高压锅炉、高压容器、机车车辆、超重机械、矿山机械、及其他大型焊接结构件。